熱熔標線涂料專用ygs抗龜裂增塑劑和聚合物改性流平劑 技術指標 全球品質、熱熔標線涂料: 重慶路鎂涂料有限公司、國內研究機構國內新研發,使用YGS抗龜裂增塑劑標線施劃后（氣溫在零下40度不龜裂）熱熔標線更抗龜裂（地面溫度75℃以上不黑線軟化點不下降）。使用YGS柔韌增塑劑能減少C5樹脂及鈦白粉用量、每噸熱熔標線涂料用C5樹脂125kg-130kg抗壓強度14.5兆帕過國檢、流動度195℃（s）38。熱熔標線涂料聚合物改性流平劑、當熱熔標線涂料配方中C5石油樹脂量達不到涂料的流動度（s）38時需要添加助流物質、YGS聚合物改性流平劑。重慶路鎂涂料有限公司爭對熱熔標線涂料的特性而特殊設計的一種優良的化學助流配方軟化點高、每噸熱熔標線涂料只需添加3kg即能達到滿意的效果。YGS抗龜裂增塑劑：本產品能粘附色粉，令著色均勻：公司所有產品均參照FDA、REACH、ROHS、PHTHALATES環保新標準生產。本產品以出口到東南亞及東盟。 重慶路鎂涂料有限公司 :http://cqlumei.b2b.hc360.com/ Hot melt marking paint for flexible, plasticizer and polymer modified leveling agent Technical indicators Global quality, hot melt marking paint leaders: Chongqing Lu magnesium coating Co. Ltd., the first domestic research institutions in the latest development, the use of YGS flexible plasticizer marking (after the temperature at minus 40 degrees without cracking) hot melt marking more anti cracking (ground temperature above 75 ℃ not black linesoftening point does not decline). The use of YGS flexible plasticizer can reduce C5 resin and titanium dioxide consumption per ton of hot melt marking paint, compressive strength of C5 resin 125kg-130kg 14.5 MPa afterinspection, the fluidity of 195 ℃ (s) 38. Hot melt marking paint polymer modified leveling agent, when C5 petroleum resin hot melt marking paint formulations amount can not to paint the fluidity (s) of 38 requires adding of material flow,YGS polymer modified leveling agent. A good chemical help Chongqing Lu magnesium coating Limited company for the characteristics of hot melt marking paint and special design flow formula of high softening point, per ton of hot melt marking paint simply add 3kg can achieve satisfactory results. YGS flexible plasticizer: This product can adhereto the toner, color uniformity: all the products of the company are referring to FDA, REACH, ROHS, PHTHALATESenvironmental protection standard production. The products are exported to Southeast Asia and asean.. Chongqing Lu magnesium coating Co. Ltd. Technical support website: http://cqlumei.b2b.hc360.com/